Selective conversion of CO₂ into dimethyl ether over hydrophobic and gallium-modified copper catalysts

hydrogenation of CO₂-to-DME via cascade catalysis involving methanol synthesis and methanol condensation to DME over a supported copper catalyst. However, high DME selectivity was only achieved at low conversion of CO₂, resulting in poor one-pass productivity.

When the CO₂ conversion increased, abundant by-products of CO, methanol, and hydrocarbons were produced. A recent trend is CO₂ to DME conversion over bifunctional catalysts, such as acid oxide-supported copper nanoparticles, but their performance is still unsatisfactory. In addition, the copper nanoparticles were sintered during catalysis, resulting in poor durability.

Recently, a research team led by Prof. Feng-Shou Xiao and Prof. Liang Wang from Zhejiang University, China, has overcome these limitations by developing a highly active, selective, and durable copper nanoparticle catalyst for converting CO₂ to DME. This was achieved by loading Cu nanoparticles onto hydrophobic and Ga-modified silica supports. The Ga-modified silica provided moderate acidity for methanol dehydration to DME, which hindered deep dehydration to hydrocarbons.

Importantly, the hydrophobic catalyst surface efficiently hinders the sintering of the Cu nanoparticles, which is usually triggered by water and methanol. Consequently, under the following reaction conditions (6000 mL g_cat^–1·h^–1, 3 MPa, 240 °C), the CO₂ conversion of 9.7%, DME and methanol selectivities of 59.3% and 28.4%, and CO selectivity of only 11.3% were obtained. In a continuous evaluation for 100 h, the performance was well maintained without any deactivation trend, outperforming the general supported Cu catalysts.

The research is published in the Chinese Journal of Catalysis.

More information:
Hangjie Li et al, Selective hydrogenation of CO2 into dimethyl ether over hydrophobic and gallium-modified copper catalysts, Chinese Journal of Catalysis (2023). DOI: 10.1016/S1872-2067(23)64535-8